- Overview
- Product Description
Basic Info.
Model NO.
solar glass
Certification
ISO 9001
Application
Solar Parts
Material
Tempered Glass
Used for
Solar Panel
Color
Transparant
Glass Thickness
1.6-4mm
Light Transmittance
>92.4%
Transport Package
Wood Package
Trademark
QYD
Origin
China
HS Code
7007190000
Production Capacity
240 Million M2
Packaging & Delivery
Package Size
2500.00cm * 1250.00cm * 970.00cm
Package Gross Weight
3500.000kg
Product Description
As the biggest glass supplier in China, We're the annealing lehr roller supplier in CHINA more than 50 years,also we are the big glass rolling machine& pattern, solar glass roller manufacturer, we still can supply various of solar glass&pattern glass&tempered glass etc.
We hold 90% market share in China. AGC, Saint-Gobain, Corning, Pilkington, CNUD, HORN, HFT, Fives-stein etc are our long-term cooperating customers.
Light Transmittance: ≥92.4%
Iron Content (Fe2O3): ≤120ppm
Heat Conductivity (20ºC): 1.06w/m•K.
Overall Bow: ≤0.2%.
Density: 2.5g/cm3
Young's Modulus: 73GPa
Tensile Strength: 42MPa
Thermal Expansion Coefficient: 9.03*10-6
Softening Point: 720ºC
Annealing Point: 570ºC
Strain Pont: 500ºC.
| Specification | |||||
| Solar Direct Transmission | ≥91.6% | ||||
| Light Transmittance | ≥92.4% | ||||
| Iron Content (Fe2O3) | ≤120ppm | ||||
| Heat Conductivity (20ºC) | 1.06w/m•K. | ||||
| Overall Bow | ≤0.2%. | ||||
| Density | 2.5g/cm3 | ||||
| Young's Modulus | 73GPa | ||||
| Tensile Strength | 42MPa | ||||
| Thermal Expansion Coefficient | 9.03*10-6 | ||||
| Softening Point | 720ºC | ||||
| Annealing Point | 570ºC | ||||
| Strain Pont. | 500ºC. | ||||
Photovoltaic transmission ratio: the direct transmission ratio of
sunlight in the band range of 380 nm to 1100 nm in the response range of
crystalline silicon photovoltaic cells.
Thickness deviation: the difference between the thickness of the glass
and the nominal size.
Thickness difference: the difference between the maximum value and the
minimum value of the thickness measurement value in the same piece of
glass.