Basic Info.
Model NO.
EVA01
Type
Float Glass
Shape
Curve
Appearance
Curved
Structure
Solid
Layer Type
Bullet-Resistant Glass
Function
Bullet-proof
Intermediate Film
PVB
Melting Point
High Temperature
Production
Wet Laminated Glass
Color
Clear
Usage
Building, Window
Visible Light Transmittance
85%
Haze
0.4%
Yellow Index (Yi)
10
Water Absorption
0.3%
Tensile Strength
22MPa
Elongation
200%
Transport Package
Wooden Carton
Specification
0.38mm, 0.76mm, 1.14mm, 1.52mm
Trademark
Jiaxing
Origin
China
HS Code
39201090
Production Capacity
200000000000sqm/Month
Packaging & Delivery
Package Size
140.00cm * 50.00cm * 50.00cm
Package Gross Weight
50.000kg
Product Description
Introduction:
PVB interlayer film is a polymer material made from polyvinyl butyral and plasticizer through plasticization, formed by pressuring with other additives. Characterized by transparency, resistance to heat, cold and humidity, and high mechanical strength, it is particularly suitable to be used as bonding material for inorganic glass, for laminated safety glass production.
Safety glass is composed of two or more pieces of glass with PVB interlayer film in between by heating and high pressure. The laminated glass has special properties such as anti-penetration, sound proof, thermal insulation, anti-UV rays, resistance to heat and cold. In addition, the reflection coefficient of PVB interlayer film is very close to that of glass itself. So the laminated glass remains the same purity and transparency as ordinary glass.
Features:
High mechanical strength
Resistance to heat, cold and humidity
Application:
Laminated safety glass.
Automotive glass
Typical Specifications:
Architechtural grade
| Thickness | Available width(mm) | Length |
| 0.38mm | 600-2850 | 400m |
| 0.76mm | 600-2850 | 200m |
| 1.14mm | 600-2850 | 150m |
| 1.52mm | 600-2850 | 100m |
| Thickness&color | Available width/shade width(mm) | Length |
| 0.38mm/clear | 600-2850/0 | 400m |
| 0.38mm/blue,green,grey | 600-2850/0-400 | 400m |
| 0.45mm/clear | 600-2850/0 | 350m |
| 0.45mm/blue,green,grey | 600-2850/0-400 | 350m |
| 0.76mm/clear | 600-2850/0 | 200m |
| 0.76mm/blue,green,grey | 600-2850/0-400 | 200m |
Technical data
| 0.38mm | 0.76mm | 1.52mm | ||
| Color | Achromatic, or slightly yellow, transparent | |||
| Appearance | Smooth surface without wrinkle | |||
| Foreign particles | ≤0.05mm2 | No more than 3 in each roll; add 1 meter at each of them | ||
| >0.05mm2 | not allowed | |||
| Size | Width(mm) | 600-2850 | ||
| Length(m) | 400 | 200 | 100 | |
| Length tolerance(mm) | +0-5 | +0-2 | +0-1 | |
| Width tolerance(mm) | +0-15 | +0-15 | +0-15 | |
| Thickness tolerance(mm) | ±0.02 | ±0.02 | ±0.03 | |
| Moisture Content(%) | <0.5 | <0.5 | <0.5 | |
| Tensile Strength(Mpa) | ≥20 | ≥20 | ≥20 | |
| Breaking Strength(%) | ≥200 | ≥200 | ≥200 | |
| Haze(%) | Archetectural | <0.4 | <0.7 | <1.2 |
| Automotive | <0.3 | <0.5 | <0.8 | |
| Shrinkage(%)60 ºC,15 min | <8 | <4 | <2 | |
| Transmittance(%) | ≥88 | ≥88 | ≥88 | |
| Elongation at break(%) | ≥160 | ≥160 | ≥160 | |
| Adhesive strength (Mpa) | ≥8.0 | ≥8.0 | ≥8.0 | |
| UV aging test(750w uv light, 100h)(%) | Change rate ≤2 | |||
| Heat aging test(70±2 ºC,humidity≥90% | After 48 hours, the sample does not change | |||